Alloy 32550 (super duplex 255) is a super duplex stainless steel supplied in the hot worked and annealed condition. It achieves higher strengths than most stainless steels and alternative corrosion resistant alloys, offering the potential to reduce section size and therefore weight and cost.
As a 25% Cr alloy, with significant additions of copper, Alloy 32550 offers excellent corrosion resistance in a wide variety of corrosive chemicals including sulphuric, nitric and phosphoric acid. In seawater and other chloride containing environments it also provides outstanding resistance to pitting and crevice corrosion, with Critical Pitting Temperature exceeding 50°C. Excellent ductility and impact strength at both ambient and sub-zero temperatures combine with a high resistance to abrasion, erosion and cavitation erosion.
Listed in NACE MR 01 75 for sour service and having gained ASME Approval for Pressure Vessel applications, Alloy 32550 is tested to the highest degree using tests designed to guarantee that the trade-marked product possesses high integrity, a correct phase balance and the absence of sigma and other deleterious phases.

SUPER DUPLEX STEEL UNS 32550 (SA 182 F - 61 / DIN 1.4507 / FERRALIUM 255)

Alloy 32550 (super duplex 255) is a super duplex stainless steel supplied in the hot worked and annealed condition. It achieves higher strengths than most stainless steels and alternative corrosion resistant alloys, offering the potential to reduce section size and therefore weight and cost.
As a 25% Cr alloy, with significant additions of copper, Alloy 32550 offers excellent corrosion resistance in a wide variety of corrosive chemicals including sulphuric, nitric and phosphoric acid. In seawater and other chloride containing environments it also provides outstanding resistance to pitting and crevice corrosion, with Critical Pitting Temperature exceeding 50°C. Excellent ductility and impact strength at both ambient and sub-zero temperatures combine with a high resistance to abrasion, erosion and cavitation erosion.
Listed in NACE MR 01 75 for sour service and having gained ASME Approval for Pressure Vessel applications, Alloy 32550 is tested to the highest degree using tests designed to guarantee that the trade-marked product possesses high integrity, a correct phase balance and the absence of sigma and other deleterious phases.

Alloy 32760 is a super duplex stainless steel supplied in the hot worked and solution annealed condition. As a super duplex stainless steel, it combines the desirable aspects of both austenitic and ferritic grades. The higher chromium, molybdenum and nitrogen contents result in a Pitting Resistance Equivalent number (PREN) of >40, providing pitting and crevice corrosion resistance superior to austenitic and duplex stainless steels in almost all corrosive media, and a Critical Pitting Temperature exceeding 50°C nb. versions of the PREN formula also include Was a positive influence on overall pitting resistance. It provides higher strength than both austenitic and 22% Cr duplex stainless steels, and is listed in NACE MR 0175 for sour service and ASME for pressure vessel applications.

Chemical composition of ASTM A182 F51 Duplex Steel Bars / ASTM A182 F51 Round Bars:

Element: Percentage

Carbon, C: 0.30 max
Chrome, Cr: 21.0-23.0
Manganese, Mn: 2.00 max
Molybdenum, Mo: 2.50-3.50
Nitrogen, N: 0.08-0.20
Nickel, Ni: 4.50-6.50
Phosphorus, P: 0.030 max
Sulfur, S: 0.020 max
Silicon, Si: 1.00 max

Alloy 32750 is a super duplex stainless steel supplied in the solution annealed condition. As a super duplex stainless steel, it combines the desirable aspects of both austenitic and ferritic grades. The higher chromium, molybdenum and nitrogen contents result in a Pitting Resistance Equivalent number (PREN) of >41, providing pitting and crevice corrosion resistance superior to austenitic and duplex stainless steels in almost all corrosive media, and a Critical Pitting Temperature exceeding 50°C. Supplied in the annealed condition, it achieves yield strengths of 80ksi (550Mpa), greater than most austenitic and duplex stainless steel grades. It cannot be hardened by heat treatment but can be strengthened by cold working. It also exhibits a low coefficient of thermal expansion and higher heat conductivity than austenitic steels and is suitable for working temperatures up to 300°C. Alloy 32750 is listed in NACE MR 0175 for sour service and having gained ASME Approval for Pressure Vessel applications it can be used in a wide variety of applications.